A quasicrystalline Al-Fe phase has been formed by room-temperature ion mixing of AI-Fe multiple layers with no additional postannealing. The quasicrystalline phase was dispersed as grain in an amorphous matrix. The size of the grains was about 10-30nm, and the composition was determined to be Al80Fe20. The structure of the quasicrystalline phase was identified by calculating some 20 sharp diffraction rings in the selected-area diffraction pattern and found to be similar to that of the rapidly quenched AI-Mn quasicrystalline phase.