Temperature dependence of the effective permeability of the resin‐molded Sendust alloys
作者:
T. Tanaka,
M. Mino,
M. Okada,
M. Homma,
期刊:
Journal of Applied Physics
(AIP Available online 1985)
卷期:
Volume 57,
issue 8
页码: 4252-4254
ISSN:0021-8979
年代: 1985
DOI:10.1063/1.335475
出版商: AIP
数据来源: AIP
摘要:
The effective permeability ( &mgr;eff) of the ring Sendust alloys (Fe‐9–10 wt. % Si‐5–7 wt. %Al), molded with Epoxy resin, was measured in the temperature range of −10 to 70 °C. The &mgr;effof the alloys in molded condition measured at 20 °C is smaller than that in unmolded condition. The high values of the &mgr;effat 20 °C of the molded alloys were obtained from the alloys in which magnetostriction constants (&lgr;s) were close to zero. The temperature dependencies of the &mgr;efffor the studied alloys in the unmolded condition are very similar, but after molding they are classified into four variations depending on the value of &lgr;s. When the alloys have large positive or negative values of &lgr;s, the &mgr;effincreases or decreases monotonically with increasing temperatures, but for the alloy with &lgr;s&bartil;0, the &mgr;efftemperature dependence is complex. These behaviors of the &mgr;effwith temperature are interpreted on the basis of the induced stress, initiating from the differences in thermal expansion between alloys and Epoxy resin. The &mgr;effof the molded alloys was mainly dominated by the induced uniaxial magnetic anisotropy (Ku) by the tangential and axial compressive stresses in the molded ring alloys.
点击下载:
PDF
(240KB)
返 回