Thin polycrystalline films made from a base composition of Pb0.92Bi0.07La0.01(Fe0.405Nb0.325Zr0.27) O3exhibited a spontaneous polarization of 10 to 20 &mgr;C per square centimeter, hysteresis‐loop squareness ≥0.75, coercivity≤15 kV/cm, Curie temperature≃150°C, resistivity≃1011&OHgr;·cm, and initial dielectric constant of about 1000. In a pulsed‐life test, one such film was repetitively switched in 300 nsec by 20‐V applied pulses for more than 2×1011polarization reversals before the test was terminated for convenience.