In this work we provide the report on the preparation of a bulkn‐type NdCeCuO superconductor using a high‐pressure high‐temperature sintering procedure. The superconductor was obtained by sintering as‐prepared material at 4.0 GPa at 530 °C for 20 min and required no additional reducing treating. The sample shows a higher onset temperatureTcon(32 K), a higher zero resistance temperatureTc0(22 K), and a much lower resistivity than a standard bulk sample. Indeed the room‐temperature resistivity and the quasimetallic resistivity in the normal state for our polycrystalline sample are similar to those of single crystals. This high‐pressure sintering procedure reduces weak link effects and opens the possibility of preparing high‐quality bulkn‐type superconductors.