Extrusion of AI–Zn–Mg–Cu–Zr alloys
作者:
BalasubramanianP. K.,
期刊:
Materials Science and Technology
(Taylor Available online 1985)
卷期:
Volume 1,
issue 6
页码: 470-474
ISSN:0267-0836
年代: 1985
DOI:10.1179/mst.1985.1.6.470
出版商: Taylor&Francis
数据来源: Taylor
摘要:
AbstractFour aluminium alloys of different zinc/magnesium ratio have been studied under various extrusion conditions. The alloys were cast in steel book moulds and subjected to initial thermomechanical treatments. Studies were made of hot extrusions and cold hydrostatic extrusions and in each case the changes in the extrusion parameters were analysed. An attempt has been made to explain some of the extrusion defects which appeared in various extruded sections. The extrusion speed was found to be crucial, since sections developed surface cracks at higher speeds. The extrusion speed was also found to vary inversely with the extrusion ratio, with higher speeds at low ratios. A well defined solute–depleted weld zone was observed on each of the four faces of a square tube extruded using a porthole die. Thermal treatment was not found to improve this weak weld zone. Tubes extruded using a floating-mandrel die withstood pressure testing up to 550 MPa.MST/43
点击下载:
PDF (3036KB)
返 回