The Y‐Ba‐Cu‐O film prepared by chemical vapor deposition showedTc=91.5 K andBc2(77.3 K)=60 T defined by zero resistance. TheJcvalues measured at 77.3 K were 7.8×105A/cm2atB=0 and 1.0×105A/cm2at 16 T, magnetic fields perpendicular to thecaxis. Small disk‐shaped precipitates possibly regarded as strong flux pinning centers in the Y‐Ba‐Cu‐O films were observed using transmission electron microscopy. The evaluation ofJcrelated to the concentration and configuration of the precipitates was in reasonable agreement with the measuredJcvalues.