PbCrO3has been synthesized in the high‐pressure ``belt'' apparatus from PbO and CrO2at 1150°C and a pressure in excess of 50 kbar. Single‐crystal and powder x‐ray diffraction at room temperature show the compound has the cubic perovskite structure witha0=4.00 Å. No deformation of the cubic structure was discerned in neutron diffraction patterns at 77° and 4.2°K. At low temperature the magnetic moments of the chromium atoms are ordered in the antiferromagneticG‐type structure in which the spins on each Cr are antiparallel to those of the six nearest neighbors. Assuming the magnetic form factor of chromium can be approximated by that of Cr3+, the magnetic intensities give a moment of 1.9 &mgr;Bper chromium atom, approximately the spin value for Cr4+(3d2). The temperature dependence of the (111) magnetic peak was measured and the results fitted to a Brillouin function withTN≈240°K. The magnetic susceptibility does not show a maximum at the Ne´el point but does obey a Curie‐Weiss law aboveTN, consistent with the neutron‐diffraction results.