Microstructure and Mechanical Properties of Hot‐Pressed Silicon Carbide‐Aluminum Nitride Compositions
作者:
Youren Xu,
Avigdor Zangvil,
Martine Landon,
François Thevenot,
期刊:
Journal of the American Ceramic Society
(WILEY Available online 1992)
卷期:
Volume 75,
issue 2
页码: 325-333
ISSN:0002-7820
年代: 1992
DOI:10.1111/j.1151-2916.1992.tb08182.x
出版商: Blackwell Publishing Ltd
关键词: silicon carbide;aluminum nitride;microstructure;mechanical properties;solid solutions
数据来源: WILEY
摘要:
A flexural strength of up to 1 GPa was achieved in SiC‐AIN materials and is attributed to a dense, equiaxial grain structure of the 2H(δ) SiC‐AIN solid solution, with a relatively uniform grain size of ∼ 1 μm. The strength was found to decrease with increasing grain size. While the β→α phase transformation and the formation of various metastable polytypes make microstructural control difficult in SiC materials, excellent control is facilitated in SiC‐AIN materials as a result of the stable 2H solid solution. Several mechanisms of grain refinement during the β→ 2H transition were observed, most notably the direct formation of several 2H grains from a single β grain. In addition, grain growth is limited by the diffusion‐controlled nature of the transition. These mechanisms could be utilized to achieve even higher strength values, with potentially higher reliability of the materials in stru