AbstractSteels containing various combinations of microalloying elements (Nb, V, and Ti) were welded at heat inputs from 3 to 6 kJ mm−1. It was shown by detailed crack tip opening displacement fracture toughness testing of coarse grained heat affected zone (HAZ) regions in single pass weld deposits that the poorest toughness properties were exhibited by steel containing a combination of Nb, V, and Ti. Steel microalloyed with only titanium had the best HAZ fracture toughness at all heat input levels. Detailed microstructural analysis, grain size measurement, hardness, and precipitation in HAZ regions were evaluated to explain the fracture toughness properties observed.MST/887