A procedure suitable for laboratory practice is described to prepare large‐area self‐supporting silicon thin crystals with (100), (110) and (111) orientations. Windows up to 2 cm in diameter and 2000 A˚ in thickness can be produced. Variation in the thickness across the sample can be as low as ±60 A˚ as measured by4He+backscattering spectrometry.