1. |
Experimental study of the effect of gas injection parameters on the bath mixing intensity induced during steelmaking |
|
Archiv für das Eisenhüttenwesen,
Volume 62,
Issue 2,
2016,
Page 47-53
Satish C. Koria,
S. Pal,
Preview
|
PDF (1061KB)
|
|
摘要:
The present study is concerned with the evaluation of the bath‐mixing intensity induced by gas injection during steelmaking. The rate constant for the process of mass transfer between the two cold‐model simulated immiscible liquids (water/oil) is employed as the criterion of judgement of bath‐mixing intensity. Gas is either injected from the bottom alone or simultaneously from top and bottom. Bath‐mixing criterion is successfully correlated with the mixing power. Increase in bottom injection rate is found to increase the rate constant. In the simultaneous injection lance distance, and top and bottom gas‐injection rates are shown to be the relevent independent dynamic parameters. From the comparison of the rate constants between pure bottom and simultaneous injection and pure top and simultaneous injection, it is asserted that the simultaneous injection provides more operational flexibility, better control of slag formation and refining rates as per blow requirements and steel grades. However, some minimum gas is required to realize the operational benefits.
ISSN:0003-8962
DOI:10.1002/srin.199101249
出版商:Wiley
年代:2016
数据来源: WILEY
|
2. |
Einfluß des Sauerstoffs auf die Ausbildung von Aluminiumoxiden in Eisenschmelzen |
|
Archiv für das Eisenhüttenwesen,
Volume 62,
Issue 2,
2016,
Page 54-59
Eberhard Steinmetz,
Christoph Andreae,
Preview
|
PDF (1394KB)
|
|
摘要:
Die Ausbildung und Beeinflussung von Aluminiumoxiden bei Reoxidation wurden in Laborschmelzen mit einer kombinierten Sauerstoff‐Meß‐ und Dosierzelle untersucht. Die Konzentrationsgrenzen und die Stoffstromdichten, die für die Bildung bestimmter Einschlußformen bestimmend sind, wurden in vordesoxidierten Proben ermittelt. Zusätzlich wurde das Verhalten bei veränderlichen Sauerstoffstromdichten und bei gleichzeitiger Beaufschlagung mit Sauerstoff und reinem Aluminium von gegenüberliegenden Seiten aus untersucht. Aus den generellen Richtungen der Stoffströme darf möglicherweise nicht auf die örtlich aktuellen Stoffströme geschlossen werden, da bestimmte Einschlußformen an zunächst nicht erwarteten Stellen, aber reproduzierbar, auftraten. Grenzflächenaktive Wirkung des in Eisen gelösten Sauerstoffs ist als Ursache nicht auszuschließen.Umbildungen in der Morphologie oder Auflösungen von schon gebildeten Phasen fanden – zumindest unter den hier vorliegenden Versuchsbedingungen – nicht statt, wohl aber Neubildungen an anderen Orten nach der bekannten Abfolge der Einschlußbildung.
ISSN:0003-8962
DOI:10.1002/srin.199101250
出版商:Wiley
年代:2016
数据来源: WILEY
|
3. |
Untersuchungen im System Kalkoxid‐Vanadiumpentoxid |
|
Archiv für das Eisenhüttenwesen,
Volume 62,
Issue 2,
2016,
Page 60-65
Yizhong Yuan,
Preview
|
PDF (815KB)
|
|
摘要:
Das System CaO‐V2O5ist in dieser Arbeit mit Hilfe verschiedener Methoden (Abschreckmethode, isotherme Sättigungsversuche, chemische und thermische Analysen sowie mikroskopische und röntgenographische Analysen) untersucht worden. In diesem Zweistoffsystem treten fünf nonvariante Gleichgewichte bei 615, 755, 995, 1 340 und 1 365 °C auf. Es existieren die Verbindungen CaO·V2O5, 2 CaO·V2O5, 3 CaO·V2O5und 4 CaO·V2O5. Bis auf C4V schmelzen alle Verbindungen kongruent und zwar bei 775, 1015 bzw. 1 405 °C. C4V zerfällt inkongruent bei 1 365 °C. In dem heterogenen Gebiet zwischen C4V und CaO existiert keine weitere Verbindung mit höherem Kalkgehalt als dem von 4 CaO·V2O5.
ISSN:0003-8962
DOI:10.1002/srin.199101251
出版商:Wiley
年代:2016
数据来源: WILEY
|
4. |
The constitutive behaviour of a Nb‐V HSLA steel in the temperature range of 900 to 975 °C |
|
Archiv für das Eisenhüttenwesen,
Volume 62,
Issue 2,
2016,
Page 66-71
Fengyin Wang,
John Gustav Lenard,
Preview
|
PDF (938KB)
|
|
摘要:
Isothermal true‐stress true‐strain flow curves of a Nb‐V HSLA steel (0.13% C‐1.55% Mn‐0.028% Nb‐0.059% V) are presented in this paper. Constitutive relations, valid at temperatures from 900 to 975 °C and at rates of strain from 0.005 to 5 s−1, are derived. It is found that an Arrhenius‐type equation, with a digital data bank storing its constants for different levels of normalized strains, represents the material's resistance to deformation adequately.
ISSN:0003-8962
DOI:10.1002/srin.199101252
出版商:Wiley
年代:2016
数据来源: WILEY
|
5. |
Subgrain growth during creep of a tempered martensitic 12% Cr‐steel |
|
Archiv für das Eisenhüttenwesen,
Volume 62,
Issue 2,
2016,
Page 72-74
Wolfgang Blum,
Stefan Straub,
Preview
|
PDF (481KB)
|
|
摘要:
The results of Nilsvang, Eggeler and llschner on subgrain growth in X 20 CrMoV 12 1 during creep are interpreted in terms of dynamic subgrain growth. It turns out that relatively large strains are needed to establish the steady‐state subgrain structure, implying that the technically relevant part of creep occurs in the transient range.
ISSN:0003-8962
DOI:10.1002/srin.199101253
出版商:Wiley
年代:2016
数据来源: WILEY
|
6. |
Metallkundliche Untersuchungen am Grundwerkstoff und an Schweißverbindungen des 9%‐Chromstahles X 10 CrMoVNb 9 1 |
|
Archiv für das Eisenhüttenwesen,
Volume 62,
Issue 2,
2016,
Page 75-82
Fritz Brühl,
Horst Cerjak,
Paul Schwaab,
Heinz Weber,
Preview
|
PDF (2357KB)
|
|
摘要:
Umfangreiche Untersuchungen zur Ausweitung des Einsatzbereiches warmfester ferritischer Stähle mit 9 bis 12 % Cr auf 600 °C führten zur Entwicklung des Stahles X 10 CrMoVNb 9 1 (P 9 1 bzw. T 9 1 nach ASTM‐A 335). Wegen der hohen Einsatztemperaturen treten unter Zeitstandbeanspruchung Gefügeänderungen auf, die am Grundwerkstoff und an Schweißverbindungen metallkundlich untersucht wurden.Im üblichen Lieferzustand weist der Stahl T 9 1 ein Gefüge aus angelassenem Martensit mit Ausscheidungen von Chromcarbiden M23C6auf den Grenzen der Martensitlatten und feinen, sowohl kohärenten wie inkohärenten Niob‐Vanadin‐Carbonitriden vom Typ MX im Korn auf. Unter Zeitstandbeanspruchung scheidet sich weiteres M23C6und MX sowie zusätzlich die Laves‐Phase aus. Die kohärenten MX‐Ausscheidungen beginnen zu überaltern. Erholung und Rekristallisation werden beschleunigt. Das Zeitstandverhalten dürfte im wesentlichen durch die MX‐Ausscheidungen bestimmt werden, wobei das Mengenverhältnis der Elemente Vanadin, Niob, Kohlenstoff und Stickstoff von erheblicher Bedeutung sein sollte.In Schweißverbindungen bildet sich die Zeitstandschädigung in der Regel in der WEZ nahe der Grenzlinie zum unbeeinflußten Grundwerkstoff aus. In diesem Bereich führt die kurzzeitige Erwärmung auf Temperaturen wenig über A1zur Bildung eines kohlenstoffarmen Austenits, da praktisch noch keine Carbide in Lösung gehen. Nach der Abkühlung liegt dann ein sehr weicher Martensit vor, der zudem beim üblichen Anlassen auf Temperaturen um 750 °C praktisch vollständig rekristallisiert.
ISSN:0003-8962
DOI:10.1002/srin.199101254
出版商:Wiley
年代:2016
数据来源: WILEY
|
7. |
Metallographic examination of the heat‐affected zone of a test weld in a type X 20 CrMoV 12 1 steel |
|
Archiv für das Eisenhüttenwesen,
Volume 62,
Issue 2,
2016,
Page 83-85
Karl Kussmaul,
Wolfgang Gaudig,
Siegfried Haas,
Preview
|
PDF (1148KB)
|
|
摘要:
Metallographic examination of a similar test weld in a type X 20 CrMoV 12 1 steel revealed a martensitic phase within the heat‐affected zone of the base metal adjacent to the fusion boundary. As a consequence, the heat‐affected zone displayed an excess microhardness compared with the unaffected base metal. It is shown that the occurrence of this martensitic phase can be correlated with segregations in the base metal. Due to its martensitic nature, this phase can be transformed to α‐ferrite and carbide by an additional tempering treatment subsequent to the standard post‐weld heat treatment. By this additional tempering treatment the uniformity of the microstructure of the heat‐affected zone can be considerably improved.
ISSN:0003-8962
DOI:10.1002/srin.199101255
出版商:Wiley
年代:2016
数据来源: WILEY
|
8. |
News from the Max‐Planck‐Institut für Eisenforschung GmbH |
|
Archiv für das Eisenhüttenwesen,
Volume 62,
Issue 2,
2016,
Page 86-88
Preview
|
PDF (499KB)
|
|
ISSN:0003-8962
DOI:10.1002/srin.199101256
出版商:Wiley
年代:2016
数据来源: WILEY
|