1. |
Research at Thyssen Stahl AG, Duisburg – Part 3 |
|
Archiv für das Eisenhüttenwesen,
Volume 57,
Issue 6,
2016,
Page 245-249
Preview
|
PDF (1964KB)
|
|
ISSN:0003-8962
DOI:10.1002/srin.198600761
出版商:Wiley
年代:2016
数据来源: WILEY
|
2. |
Determination of the Young's modulus of coke – a novel method |
|
Archiv für das Eisenhüttenwesen,
Volume 57,
Issue 6,
2016,
Page 250-255
Wolfgang Klose,
Hidetaka Suginobe,
Preview
|
PDF (470KB)
|
|
摘要:
Based on the Hertz contact problem of two cylinders a method was developed to determine Young's modulus of brittle materials, e.g. coke, from the indirect tensile test. The error band to be taken into account for evaluation have been discussed. As far as chamber‐oven cokes are concerned, it was possible to derive Young's moduli, which correlated well with the values found by other authors by means of static measuring methods. In addition was determined, on a semi‐empiric basis, a linear relation between Young's modulus and porosity, – relation allowing to consider the influence of coke structure as well.
ISSN:0003-8962
DOI:10.1002/srin.198600762
出版商:Wiley
年代:2016
数据来源: WILEY
|
3. |
Bestimmung von Fließkurven mit dem Warmflachstauchversuch |
|
Archiv für das Eisenhüttenwesen,
Volume 57,
Issue 6,
2016,
Page 256-261
Werner Kapellner,
Radko Kaspar,
Oskar Pawelski,
Preview
|
PDF (611KB)
|
|
摘要:
Zur Bestimmung von Fließkurven werden Warmflachstauchversuche mit dem Warmumformsimulator (Wumsi) des Max‐Planck‐Instituts für Eisenforschung durchgeführt. Aus den Meßdaten Werkzeugweg, Stauchkraft und Probentemperatur sowie aus den Abmessungen der Probe wie Anfangsdicke, Anfangsbreite und mittlere Stauchfläche werden Fließkurven unter Anwendung der elementaren Plastomechanik berechnet. Die Auswertung der Fließkurven liefert die Fließgrenze, die maximale Spannung und den Verlauf des differentiellenn‐Wertes. Weiterhin wird eine neue Methode angewendet, um die Reibungsverhältnisse beim Warmflachstauchen zahlenmäßig zu berücksichtigen. Aus dem Temperaturverlauf während der Umformung und der Kenntnis der Temperaturabhängigkeit der Fließspannung werden temperaturkorrigierte Fließkurven berechnet. An Beispielen wird erläutert, wie Fließkurven zur Interpretation metallkundlicher Vorgänge genutzt werden können, die während der Umformung ablaufen.
ISSN:0003-8962
DOI:10.1002/srin.198600763
出版商:Wiley
年代:2016
数据来源: WILEY
|
4. |
Hot workability of steels for forgings |
|
Archiv für das Eisenhüttenwesen,
Volume 57,
Issue 6,
2016,
Page 262-269
Helmut Finkler,
Günter Rennollet,
Preview
|
PDF (748KB)
|
|
摘要:
Sufficient hot ductility is one of the prerequisites for the successful forming and heat treatment of steels. The influence of chemical composition (including trace elements), of soaking and deformation temperatures, strain rate and duration of deformation was to be studied in hot tensile testing. To distinguish the different embrittling mechanisms from each other, a great number of steels with systematically varied composition were examined. Test conditions were chosen so as to give maximum agreement with actual hot working operations.In the temperature range from 1 200–600°C, which was covered by this study, hot embrittlement was only found on steels containing at least one of the elements N, Nb, Pb or Bi. Embrittlement due to MnS precipitations did not occur, as the soaking temperature was limited to max. 1 315°C and the Mn/S ratio was at least 30. Nitrogen is the main cause of hot embrittlement in commercial steels. The fact that also unalloyed, aluminium‐free steels embrittle with sufficiently low strain rate shows that nitrogen in solid solution may cause embrittlement even in the absence of nitride formers. The nitride formers accelerate the embrittling process, provided the nitrides are dissolved at soaking temperature. Aluminium, however, has a retarding effect in the presence of vanadium. Embrittlement is attributed to nitrogen atoms entering into multiple voids and micropores, where they recombine to form molecules which impede the slip of dislocations, thus leading to embrittlement. A sufficient length of the deformation operation and recrystallisation being impeded by precipitations are the prerequisites for this type of embrittlement. Titanium, by binding nitrogen at an early stage, prevents precipitation. Also in the case of embrittlement by lead and bismuth, the most conclusive explanation is that atoms of these elements accumulate in voids. Embrittlement by niobium, however, is attributed to deformation‐induced precipitation, as it only occurs on cooling from soaking to test temperature and not on direct heating to test temperature.
ISSN:0003-8962
DOI:10.1002/srin.198600764
出版商:Wiley
年代:2016
数据来源: WILEY
|
5. |
Einflüsse auf die Austenitkorngröße von Einsatzstählen |
|
Archiv für das Eisenhüttenwesen,
Volume 57,
Issue 6,
2016,
Page 270-285
Serosh J. Engineer,
Rainer Kohlmann,
Volker Schüler,
Herbert Stelzenmüller,
Preview
|
PDF (2210KB)
|
|
摘要:
Mit dem Bericht soll ein Überblick über Einflüsse der Stahlherstell‐ und Stahlverarbeitungsbedingungen auf die Austenitkorngröße von Einsatzstählen gegeben werden.Für die Feinkornbeständigkeit der Einsatzstähle haben Aluminiumnitride vor anderen Feinkornbildnern vorrangige Bedeutung. Im ersten Teil dieses Berichtes, der die Erfahrungen deutscher Stahlhersteller zusammenfaßt, werden einige dem Schrifttum entnommene, wichtige Zusammenhänge der Auflösungs‐ und Ausscheidungsbedingungen, insbesondere für Aluminiumnitride, dargestellt.Im zweiten Teil werden die wichtigsten Bedingungen der derzeit gültigen nationalen und internationalen Normen für die Austenitkorngrößenprüfung der Einsatzstähle beschrieben und kritisch verglichen.Im dritten Teil werden Ergebnisse von betrieblichen Untersuchungen und Laboruntersuchungen an unterschiedlichen Einsatzstählen mitgeteilt. Es wird der Einfluß der Fertigungsbedingungen, insbesondere der Wärmebehandlungen, der Warm‐ und Kaltumformung auf die Austenitkorngröße der Einsatzstähle gezeigt und der Versuch unternommen, die Untersuchungsergebnisse metallkundlich zu deuten.
ISSN:0003-8962
DOI:10.1002/srin.198600765
出版商:Wiley
年代:2016
数据来源: WILEY
|
6. |
Abrasive wear resistance of boron alloyed austenitic Fe—Mn—C‐steels |
|
Archiv für das Eisenhüttenwesen,
Volume 57,
Issue 6,
2016,
Page 286-291
Ingo Schmidt,
Annette Göcke,
Preview
|
PDF (1126KB)
|
|
摘要:
Alloying additions of 0.25–1.0 wt‐% B to austenitic manganese steels lead to the formation of carboborides arranged in a cell‐type microstructure. Pin abrasion tests on flint grinding paper using different dead weight loads reveal that these carboborides do not substantially improve the wear resistance due to a relatively low hardness and weak bonding to the austenite matrix. However, carboborides hardened by V, e.g., can considerably increase the abrasive wear resistance. They are very effective in a metastable austenitic matrix in which friction‐induced martensitic transformation occurs. It is the consequence of compressive stresses in the martensitic surface layer which improve the anchoring of insufficiently bonded carboborides in the matrix.
ISSN:0003-8962
DOI:10.1002/srin.198600766
出版商:Wiley
年代:2016
数据来源: WILEY
|
7. |
News from the Max‐Planck‐Institut für Eisenforschung GmbH |
|
Archiv für das Eisenhüttenwesen,
Volume 57,
Issue 6,
2016,
Page 292-298
Preview
|
PDF (761KB)
|
|
ISSN:0003-8962
DOI:10.1002/srin.198600767
出版商:Wiley
年代:2016
数据来源: WILEY
|