The characteristic formation of dark filamentary features during the rapid degradation mode of AlxGa1−xAs double‐heterostructure lasers has been observed in material with no contacts, with or without ap‐njunction, and in minimal‐strain mounting configurations. The degradation was observed in optically pumped cw lasing and nonlasing conditions with active region temperatures near and above room temperature.